Diran 410MF07
FDM Thermoplastic Filament
Diran 410MF07 is a nylon-based thermoplastic FDM® material, mineral-filled 7% by weight. It demonstrates very good toughness and impact strength combined with resistance to hydrocarbon-based chemicals. Its smooth, lubricious surface quality offers low sliding resistance.
Typical applications include jigs, fixtures and other forms of general manufacturing tooling, and is particularly effective for applications needing a non-marring interface between the tool and the work piece.
Diran 410MF07 Material Properties
Behaviour and use
Main Uses
Diran is a nylon-based material specifically formulated for the production of jigs, fixtures, manufacturing aids, etc.
The material exhibits good mechanical properties and toughness – flexible, but strong.
Also, it has high lubricity (i.e. low surface friction) which is good for wear resistance and low scratch and mar characteristics limiting damage when in contact with sensitive components.
Top Applications
- To reduce weight, lead time and cost in the production of manufacturing aids without the risk of marking your product.
- Enhanced durability, strength and wear properties over existing solutions.
- The ability to consolidate parts and improve tooling functionality and ergonomics.
FDM Material Applications
Learn how designers and engineers are using FDM Materials
Design Firm 3D Prints with Stratasys machine to refine Ideas with Speed
A Stratasys F123 series printer with GrabCAD Print™ software streamlines the shared workflow of a Design Firm and makes CAD even more responsive to fast-moving projects.
3D Printing a Space Vehicle for Mars Exploration
To design such a tenacious and specialized vehicle, NASA are 3D Printing Space Vehicle Parts. For example, about 70 of the parts that make up the rover were built digitally, directly from computer designs, in the heated chamber of a production-grade Stratasys 3D Printer.
Additive Manufacturing reduces fixture costs by 65%
Oreck uses PC thermoplastic to create custom assembly pallets for its commercial vacuum business. Oreck uses Additive Manufacturing extensively to produce prototypes, specialized assembly tools and CNC milling fixtures.
Reaching New Heights of Efficiency with Additive Manufacturing Tooling
GKN Aerospace Achieves Significant Savings with Additive Manufactured Tooling and Prototypes. GKN Aerospace (GKN) is a leading multi-technology tier one aerospace supplier, serving over 90% of the world’s aircraft and engine manufacturers.
Additive Manufacturing reduces Aerospace part lead time by 95%
Rapid Processing Solutions Inc. (Rapid PSI) is a contract manufacturer that specializes in Additive Manufacturing Aerospace parts. The company uses Stratasys 3D Production Systems to make production parts for most every large business jet manufacturer worldwide.
Diran 410MF07 Specification & Features
| Property | Test Method | Typical Values XY | Typical Values XZ/ZX |
|---|---|---|---|
| HDT @ 66psi | ASTM D648 Method B | 90 °C (194 °F) | 90 °C (194 °F) |
| HDT @ 264psi | ASTM D648 Method B | 70 °C (158 °F) | 70 °C (158 °F) |
| Tg | ASTM D7426 Inflection Point | 117 °C (243 °F) | 117 °C (243 °F) |
| Mean CTE | ASTM E831 (40 °C to 140 °C) | 55 μm/[m·°C] (31 μin/[in·°F]) | 113 μm/[m·°C] (63 μin/[in·°F]) |
| Volume Resistivity | ASTM D257 | > 1.5*1015 Ω·cm | > 1.5*1015 Ω·cm |
| Dielectric Constant | ASTM D150 1 kHz test condition | 3.58 | 3.73 |
| Dielectric Constant | ASTM D150 2 MHz test condition | 2.85 | 2.95 |
| Dissipation Factor | ASTM D150 1 kHz test condition | 0.013 | 0.014 |
| Dissipation Factor | ASTM D150 2 MHz test condition | 0 | 0.012 |
| Specific Gravity | ASTM D792 @ 23 °C | 1.16 | 1.16 |
| Mechanical Properties | XZ Orientation(1) | ZX Orientation(1) | |
|---|---|---|---|
| Tensile Properties: ASTM D638 | |||
| Yield Strength | MPa | 45 (2) | No yield |
| psi | 6,490 (220) | No yield | |
| Elongation @ Yield | % | 4.26 (0.04) | No yield |
| Strength @ Break | MPa | 40 (3) | 30 (2) |
| psi | 5,860 (440) | 4,460 (295) | |
| Elongation @ Break | % | 12 (3) | 3.1 (1.0) |
| Modulus (Elastic) | GPa | 1.69 (0.02) | 1.46 (0.02) |
| ksi | 245 (3) | 210 (3) | |
| Flexural Properties: ASTM D790, Procedure A | |||
| Strength @ Break | MPa | No break | 45 (2) |
| psi | No break | 6,770 (325) | |
| Strength @ 5% Strain | Mpa | 60 (2) | - |
| psi | 8,800 (230) | - | |
| Strain @ Break | % | No break | 3.1 (0.6) |
| Modulus | Gpa | 1.85 (0.04) | 1.47 (0.07) |
| ksi | 270 (6) | 210 (10) | |
| Compression Properties: ASTM D695 | |||
| Yield Strength | Mpa | 75 (5) | 160 (30) |
| psi | 10,980 (630) | 23,560 (4330) | |
| Modulus | Gpa | 1.54 (0.03) | 1.45 (0.02) |
| ksi | 220 (4) | 210 (3) | |
| Impact Properties: ASTM D256, ASTM D4812 | |||
| Izod, Notched | J/m | 380 (135) | 27 (5) |
| ft*lb/in | 7 (3) | 0.5 (0.1) | |
| Izod, Unnotched | J/m | 1,415 (200) | 140 (25) |
| ft*lb/in | 25 (4) | 2.6 (0.5) | |
| (1) Values in parentheses are standard deviations | |||